LQ-PVC/PET
UPG & LQ
PROPERTY | TEST METHOD | UNIT | STANDARD | |
WIDTH | / | MM | (+)6 | |
THICKNESS | ASTM D 374 | MIC | (±)3 | |
TENSILE STRENGTH | MD |
ASTM D 882 |
Mpa | ≧42.0 |
TD | ≧150.0 | |||
ELONGATION | MD |
ASTM D 882 |
KN/M | ≧350.0 |
TD | ≧60.0 | |||
HEAT SHRINKAGE | MD | ASTM D 1204 95℃/10SEC |
% | 2 |
TD | ≧50 | |||
C.O.F(IN/OUT) | µs/µk | ASTM D 1984E | -- | 0.41/0.4 |
WETTING TENSION | ASTM D 2587 | mN/m | 40 | |