LQ-CPP
UPG & LQ
CALENDERED PVC收缩膜是通过挤出，压延，拉伸和纵切制成的。 收缩率高，透明性和平整度好，收缩后无皱纹。 适用于高速自动机印刷，广泛应用于热收缩标签印刷。 厚度为35-75微米，最大拉伸宽度为3600mm。
Properties | Units | Value | |||
Thickness tolerance | micron | ±2.5 | |||
Width tolerance | mm | ±2 | |||
Weight tolerance | Kg/Roll | ±5% | |||
Density | g/cm2 | 1.36 | |||
Haze | % | ≤3 | |||
Tensile strength | MD |
Mpa | ≥55 | ||
TD | ≥125 | ||||
Elongation at break | MD |
% | ≥185 | ||
TD | ≥45 | ||||
Shrinkage | MD | 100 ℃ |
% | 0-5 | |
TD | 100 ℃ | 58-60 | |||
Thickness | micron | 50 | |||
Width | mm | 400 – 1300 | |||
Shrinkage | - | No wrinkles after shrink | |||
Feature |
- | Good flatness , excellent for machine printing | |||
CALENDERED PVC收缩膜是通过挤出，压延，拉伸和纵切制成的。 收缩率高，透明性和平整度好，收缩后无皱纹。 适用于高速自动机印刷，广泛应用于热收缩标签印刷。 厚度为35-75微米，最大拉伸宽度为3600mm。
Properties | Units | Value | |||
Thickness tolerance | micron | ±2.5 | |||
Width tolerance | mm | ±2 | |||
Weight tolerance | Kg/Roll | ±5% | |||
Density | g/cm2 | 1.36 | |||
Haze | % | ≤3 | |||
Tensile strength | MD |
Mpa | ≥55 | ||
TD | ≥125 | ||||
Elongation at break | MD |
% | ≥185 | ||
TD | ≥45 | ||||
Shrinkage | MD | 100 ℃ |
% | 0-5 | |
TD | 100 ℃ | 58-60 | |||
Thickness | micron | 50 | |||
Width | mm | 400 – 1300 | |||
Shrinkage | - | No wrinkles after shrink | |||
Feature |
- | Good flatness , excellent for machine printing | |||